MAGNETIC BEHAVIOR OF NICKEL FERRITE NANOPARTICLES PREPARED BY CO-PRECIPITATION ROUTE

Authors

  • K. Maaz Directorate of Technology, PINSTECH, P.O. Nilore, Islamabad, Pakistan
  • A. Mashiatullah Directorate of Technology, PINSTECH, P.O. Nilore, Islamabad, Pakistan
  • N. K. Qazi Directorate of Technology, PINSTECH, P.O. Nilore, Islamabad, Pakistan
  • T. Javed Directorate of Technology, PINSTECH, P.O. Nilore, Islamabad, Pakistan
  • R. M. Qureshi Directorate of Co-ordination, PINSTECH, P.O. Nilore, Islamabad, Pakistan
  • S. Karim Physics Division, PINSTECH, P.O. Nilore, Islamabad, Pakistan
  • G. Ali Physics Division, PINSTECH, P.O. Nilore, Islamabad, Pakistan

Abstract

Magnetic nanoparticles of nickel ferrite (NiFe2O4) have been synthesized by co-precipitation route using stable ferric and nickel salts with sodium hydroxide as the precipitating agent and oleic acid as the surfactant. X-ray Diffraction (XRD) and Transmission Electron Microscope (TEM) analyses confirmed the formation of single phase nickel ferrite nanoparticles in the range 8-28 nm. The size of the particles was observed to be increasing linearly with increasing annealing temperature of the sample. Typical blocking effects were observed below ~225 K for all the prepared samples. The superparamagnetic blocking temperature was found to be continuously increasing with increasing particle sizes that has been attributed to the increased effective anisotropy of the nanoparticles. The saturation moment of all the samples was found much below the bulk value of nickel ferrite that has been attributed to the disordered surface spins of these nanoparticles.

References

M. Dariel, L.H. Bennett, D.S. Lashmore, P. Lubitz, M.Rubinstein, W.L. Lechter and M.Z. Harford, J. Appl. Phys. 61 (1987) 4067.

W.D. Williams and N. Giordano, Phys. Rev. B 33 (1986) 8146.

T.M. Whitney , J.S. Jiang, P.C. Searson and C.L. Chien, Science 261 (1993) 1316.

L. Piraux, J.M. George, J.F. Despres, C. Leroy, E. Ferain, R. Legras, K. Ounadjela and A. Fert, Appl. Phys. Lett. 65 (1994) 2484.

C.J . Brumlik and C. R. Martin, Anal. Chem. 59 (1992) 2625.

Z. Cai, C.R. Martin, J. Amer. Chem. Soc. 111 (1989) 4138.

S .K. Chakarvarti and J. Vetter, Nucl. Instr. Meth. B 62 (1991) 109.

Idem., J. Microm. Microeng. 3 (1993) 57.

Idem., Radiat. Meas. 29, No. 2 (1998) 149.

I.M.L. Billas, A. Chatelain and W.A. de Heer, Science 265 (1994) 1682.

D.D. Awschalom and D.P.D. Vincenzo, Physics Today 48, (1995) 43.

M. George, A.M. John, S.S. Nair, P.A. Joy and M.R. Anantharaman, J. Magn. Magn. Mater. 302 (2006) 190.

S. Son, M. Taheri, E. Carpenter, V.G. Harris and M.E. McHenry, J. Appl. Phys. 91, No. 10 (2002) 7589.

D.H. Chen and Y.Y. Chen, J. Colloid Interface Sci. 9 (2001) 235.

J.J. Kingsley, K. Suresh and K.C. Patil, J. Mater. Sci. 25 (1990) 1305.

D.H. Chen and X.R. He, Bull. Mater.Res. 36, (2001) 1369.

S.Z. Zhang and G.L. Messing, J. Am. Ceram. Soc. 73 (1990) 61.

D.H. Chen and Y.Y. Chen, J. Colloid Interface Sci. 41 (2001) 236.

J.L. Duan, J. Liu, H.J. Yao, Dan Mo, M.D. Hou, Y.M. Sun, Y.F. Chen and L. Zhang, Materials Science and Engineering B 147, (2008) 57.

D. Mo, J. Liu, H.J. Yao, J.L. Duan, M.D. Hou, Y.M. Sun, Y.F. Chen, Z.H. Xue and L. Zhang, J. Crystal Growth 310 (2008) 612.

T. Feried, G. Shemer and G. Markovich, Adv. Mater. 13, No.15 (2001) 1158.

C. Liu, A. J. Rondinone and Z. J. Zhang, Pure Appl. Chem. 72 Nos. 1-2, (2000) 37.

T. P. Raming, A. J. A. Winnubst, C. M. van Kats and P. Philipse, J. Colloid and Interface Science 249 (2002) 346.

A. Mumtaz, K. Maaz, B. Janjua, S.K. Hasanain and M.F. Bertino, J. Magn. Magn. Mater. 266 (2007) 313.

R. Skomski and J.D.M. Coey, “Permanent Magnetismâ€, Institute of Physics Publishing Ltd., UK (1999).

K. Maaz, A. Mumtaz, S.K. Hasanain and A. Ceylan, J. Magn. Magn. Mater. 308 (2007) 289.

A. Aharoni, “Introduction to the theory of Ferromagnetismâ€, Clarendon Press, Oxford 94 (1996).

A.E. Berkowitz, J.A. Lahut, I.S. Jacobs, L.M. Levinson and D.W. Forester, Phys. Rev. Lett. 34 (1975) 594.

A.E. Berkowitz, J.A. Lahut and C.E. Van Buren, IEEE Trans. Magn. MAG-16 (1980) 184.

J.M.D. Coey, Phys. Rev. Lett. 27 (1971) 1140.

Downloads

Published

01-07-2020

How to Cite

[1]
K. Maaz, “MAGNETIC BEHAVIOR OF NICKEL FERRITE NANOPARTICLES PREPARED BY CO-PRECIPITATION ROUTE”, The Nucleus, vol. 45, no. 3-4, pp. 101–106, Jul. 2020.

Issue

Section

Articles